Abstract
The optical behaviour, stoichiometry, surface configuration of Cu2Se nanostructured thin layers prepared at different reaction times by the chemical process has been considered. The optical band gap of the deposited thin films decreases from 2.92 eV to 2.08 eV for the first transition and from 2.18 to 1.2 eV for the second transition. In addition, it was shown that Urbach energy is independent from the film thickness, and tail values of the localized states has decreased from 1.15 to 0.33 eV. It was found that the concentration of Cu: Se remains approximately constant across the depth of the deposited film at higher deposition time. The degradation efficiency of 98% was achieved by Congo red for the prepared Cu2Se thin film at optimal condition which make it a good candidate for organic dye. From these measurements and by controlling the band gap energy, the Cu2Se can find application in solar cell application.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.