The formation of interfacial metal–oxide structures on the Pt3Ni(111) bimetallic surface was investigated using scanning tunneling microscopy (STM) and X-ray photoelectron spectroscopy (XPS) techniques at near-ambient pressure (NAP). Direct observation of surface images clearly shows the occurrence of surface segregation of the sub-surface Ni depending on the surrounding gas-phase conditions. Especially, the prepared topmost Pt-skin layer of the Pt3Ni(111) is altered by Ni oxide segregation that makes an interfacial Pt-NiO1−x nanostructure with dissociated oxygen. This metal–oxide interface could provide active sites for more-efficient carbon monoxide (CO) conversion processes under mixed CO/O2 gas environments; the associated specific chemical binding energy was identified using NAP-XPS. The combined operando observations from the NAP-STM and NAP-XPS on the Pt3Ni(111) surface reveal that the interfacial metal–oxide structure is strongly correlated with the origin of the enhanced catalytic activity at thermodynamic equilibrium.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Electron Spectroscopy and Related Phenomena
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.