Abstract
In this study, an aerospace thermosetting composite was co-curing joined by Polyether-ether-ketone (PEEK) and Polyethylenimine (PEI) films, with an aim of developing advanced composite joints. The semi-crystalline PEEK films were surface activated upon a UV-irradiation technique to obtain a strong film–composite interface, while the amorphous PEI films could be directly used. The fracture behaviour of the composite joints was evaluated and compared with benchmark aerospace adhesive joints. The experimental results proved remarkable mode-I and mode-II fracture resistance of the PEEK co-cured joints at 22 °C and 130 °C, while the PEI co-cured joints exhibited excellent mode-I fracture resistance at 22 °C and mode-II fracture resistance in both testing temperature cases. Extensive elongation, tearing and fracture of the PEEK/PEI plastics were proved to be the main mechanisms for toughness enhancement. Overall, this work had successfully demonstrated the effectiveness of developing advanced composite joints via a co-curing process using high-performance thermoplastic films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.