Abstract
Tribological fatigue failure of the machined PEEK shaft was investigated through the one-point type rolling contact fatigue test between a PEEK shaft and an alumina ball, in order to explore fatigue fracture mechanism of frictional parts working at high frequency in various mechanical elements. Due to Hertzian contact of cyclic compressive stress, the subsurface crack occurred within approximately 300 μm depth from thesurface and propagated along the rolling direction. After that, the subsurface crack propagation direction changed toward the surface. The flaking occurred on the raceway of the PEEK shaft when the subsurface crack reached to the PEEK shaft surface.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.