Abstract
Based on volume of fluid (VoF) interface capturing method and shear-stress transport (SST) k-ω turbulence model, numerical simulation was performed to reveal the flow mechanism of metal melts in melt delivery nozzle (MDN) during gas atomization (GA) process. The experimental validation indicated that the numerical models could give a reasonable prediction on the melt flow process in the MDN. With the decrease of the MDN inner-diameter, the melt flow resistance increased for both molten aluminum and iron, especially achieving an order of 102 kPa in the case of the MDN inner-diameter ≤1 mm. Based on the conventional GA process, the positive pressure was imposed on the viscous aluminum alloy melt to overcome its flow resistance in the MDN, thus producing powders under different MDN inner-diameters. When the MDN inner-diameter was reduced from 4 to 2 mm, the yield of fine powder (<150 μm) soared from 54.7% to 94.2%. The surface quality of powders has also been improved when using a smaller inner-diameter MDN.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.