Abstract
Poly(3,4-ethylenedioxythiophene) nanotubes (PEDOT NTs) flexible membrane was successfully fabricated by vapor deposition polymerization (VDP) mediated electrospinning for ammonia gas detection. PVA nanofibers (NFs) were electrospun as a core part and polyvinyl alcohol (PVA)/PEDOT coaxial nanocables (NCs) were prepared by VDP method via EDOT monomer adsorption onto the electrospun PVA NFs as templates. To obtain the PEDOT NTs membrane, the PVA NFs were removed from PVA/PEDOT coaxial NCs with distilled water. PVA/PEDOT coaxial NCs and PEDOT NTs had the conductivities of 71 and 61 S cm −1 and were applied as a transducer for ammonia gas detection in the range of 1–100 parts per million (ppm) of NH 3 gas. They exhibited the minimum detectable level of ca. 5 parts per million (ppm) and fast response time (less than 1 s) towards ammonia gas. In a recovery time, the PEDOT NTs membrane sensor was ca. 30 s and shorter compared to that of the membrane sensor based on the PVA/PEDOT NCs ( ca. 50 s). In addition, sensor performance of PEDOT NTs membrane was also undertaken as a function of membrane thickness. Thick membrane sensor (30 μm) had the enhanced sensitivity and the sensitivity on the membrane thickness was in the order of 30 μm > 20 μm > 10 μm at 60 ppm of NH 3 gas.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.