Abstract
Poly(trimethylene terephthalate)/polyethylene glycol (PTT/PEG) copolymers, with PEG content ranging from 27.2 to 47.4 wt%, were synthesized by melt copolycondensation. Wide-Angle X-ray diffractometer revealed that all copolymers had the same crystal structure of homo-PTT at room temperature. All copolymers could form ring-banded spherulites, and band spacing increased with increasing PEG content at a given crystallization temperature. Nonisothermal crystallization morphology of copolymers was greatly influenced by cooling rate. When the cooling rate was 2.5 °C/min or lower, banded patterns were absent, whereas when the cooling rate was 20 °C/min or higher, a novel crystal morphology composed of non-banded spherulites (central part) and ring-banded spherulites with decreasing band spacing along the radial growth direction was observed. Moreover, the size of the non-banded spherulitic part decreased with increasing cooling rate. Finally, the nonisothermal crystallization kinetics of copolymers were analyzed and only the Mo method was satisfactory to accurately describe this system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.