Abstract
Non-destructive characterization of surface microstructure of an engineering component is an important parameter to assess its fitness to function in the given service conditions. The paper describes various case studies performed in authors’ laboratory involving use of portable X-ray diffraction based residual stress analysis system to examine and understand the micro-structural state of the investigated surface. A significant decrease in full width at half maximum (FWHM) of gamma(311) diffraction peak from about 4.2° in the cold worked state to about 2.5° in the annealed/surface melted state was recorded for austenitic stainless steel. In case of 0.4% carbon steel there is sharp increase in FWHM of alpha(211) diffraction peak from about 2° in the as received condition to about 5-6° in the laser hardened condition. Crystallographic texture developed during electro-plating of chromium on stainless steel, could be detected from the strong intensity of alpha (211) peak of chromium at about 19° to the surface normal with respect to all other X-ray inclination angles (ѱ) during residual stress measurement. The results show that FWHM and intensity variation of the diffraction peak are two sensitive parameters for characterization of surface microstructure. Change in FWHM has been used to detect machining-induced cold deformation and evolution of re-crystallized grains in austenitic stainless steel and formation of hard martensite in laser transformation hardened ferritic steel. Variation in the intensity of diffracted peak with respect to X-ray inclination angle provided valuable information regarding crystallographic texture in hard chrome plated deposits.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.