Abstract
ABSTRACT The thick titanium nitrides coating was fabricated on LZ91 alloy by surface mechanical nano-alloying (SMNAT) combined with gas nitriding. Experimental results showed that a nanostructured titanium coating with thickness of 50–80 μm was formed on surface of LZ91 alloy by SMNAT with pure titanium powders for 30 min. By adding of the aluminium powders into titanium powders during the SMNAT, a thicker Ti-Al composite coating with improved continuity and uniformity was obtained. After nitriding at 450°C, the whole Ti and Ti-Al coating were successfully nitrided. The surface layer of nitrided Ti coated sample is mainly composed of TiN, Ti2N, TiN0.3, TiN0.61 and Ti4N2.33 phases and the surface layer of nitrided Ti-Al coated sample is composed of Ti2N, TiN0.9, TiN0.3, Ti4N2.33, AlN, Ti3Al2N2 and AlTi2N phases. The hardness measurements demonstrated that the surface hardness of nitrided Ti coated and nitrided Ti-Al coated samples reached to 634 and 734 HV, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.