Abstract
In this research, nickel metal of three different morphologies including nanostar, icosahedra, and microsphere structures were synthesized. It was found nanostar nickel revealed the Ni(111) crystallographic plane with particle size in the range of 150-200 nm and BET surface area of 13 m2/g. The icosahedra nickel also showed the Ni(111) crystallographic plane with larger particle size (300-400 nm) and BET surface area of 20 m2/g, whereas microsphere nickel exhibited the relatively large cluster size (approximately 3 microm) and BET surface area (114 m2/g) as a result of an aggregation of Ni(101) nanoplates. The obtained nickel catalysts were tested for the activity in carbon dioxide reforming with methane. Based on the similar specific surface area of catalysts, nanostar nickel showed the highest carbon dioxide and methane conversions due to its crystallographic structure. At 700 degrees C, nanostar nickel catalyst exhibited the highest carbon dioxide and methane conversions of 17.6 and 10.5 times higher than those of microsphere nickel catalyst, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.