Abstract
Reactive milling of nickel oxide and aluminium powders corresponding to the stoichiometric reaction 3NiO + 5Al resulted in the formation of intermetallic matrix composite NiAl-Al2O3, with 28 wt% of alumina. Prolongation of the milling process allowed obtaining the microstructure with nanosize range of crystallites of both phases, as showed XRD measurements and TEM observations. The refinement of microstructure was accompanied with an increase of lattice strain as a result of ball milling. The particles size and morphology changed from several tens of micrometers and polyhedron shape observed immediately after the reaction took place, to several micrometers and spherulitic shape after long-term milling.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.