New insights into the effect of glass addition on the piezoelectric and thermal stability properties of (Ba0.85Ca0.15)(Ti0.9Zr0.1)O3 Pb-free ceramic by defect engineering of MPB

Abstract

Lead-free piezoceramics with superior piezoelectric properties don't meet the requirements of practical applications due to their lower phase transition temperature and poor thermal stability. In the present work, we report a new insight into the effect of glass phase on the piezoelectric, Curie temperature and thermal stability of (Ba0.85Ca0.15)(Ti0.9Zr0.1)O3 (BCZT) ceramic. Unlike traditional glass materials with more than 80% of B2O3 and SiO2 as glass formers, our approach is to fabricate a glass phase (Ba0.85Ca0.15)(Ti0.9Zr0.1)O3-0.05B2O3 (abbreviate BBCZT) with the same elements and concentrations as the ceramic phase. The ceramics-doped glass samples with the composition [(1-x)BCZT-xBBCZT], where x=(0.0, 0.025, 0.05, 0.075 and 0.1 wt%), were sintered according to the glass phase content. The effect of BBCZT glass composition on the crystal structure, dielectric, ferroelectric and piezoelectric properties of BCZT was investigated in detail. X-ray diffraction revealed that the addition of glass phase causes a defect engineering of the tricritical triple point of BCZT ceramic, where the tetragonal (T) and rhombohedral (R) phases were suppressed by the addition of glass phase and the T-phase has completely vanished at x = 0.05. The maximum value of permittivity (ε = 4102) and converse piezoelectric coefficient (d*33 = 1150 Pm/V) were achieved for the 0.975BCZT-0.025BBCZT sample at ambient temperature. Furthermore, the diffusion coefficient (γ) and Curie temperature (Tc) were observed to increase beyond x = 0.025, indicating enhanced thermal stability of BCZT at high glass content. These results qualify that the addition of (BBCZT) can enhance piezoelectric properties, phase transition temperature and thermal stability of BCZT ceramic which can meet wide requirements of practical applications.