Abstract
Near-net shape forming of the turbine wheel with a hollow internal structure was realized by adopting the die with side core-pulling mechanism. MIM418 turbine wheel with relative density above 99.5% is obtained by the combination of vacuum sintering and hot isostatic pressing. A high volume fraction (57%) of near cuboidal γ′ phase with average particle size of 0.52 μm is formed in γ matrix. Small amount of discrete carbides with size of 0.2-0.4 μm is distributed uniformly on grain boundaries and within grains. The tensile strength, yield strength, and ductility of MIM418 superalloy reach 1425 MPa, 1004 MPa, and 19.4%, respectively, which are much higher than that of the cast K418 superalloy.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.