In this study, high-resolution transmission electron microscopy (HRTEM) was employed to characterize the nanostructure of strontium-substituted hydroxyapatite (Sr-HA) and its evolution following in vitro immersion in physiological solutions. HRTEM images showed that the substitution of Sr induced local distortions in the hydroxyapatite (HA) lattice: minor levels of edge dislocations were detected at low doping contents of Sr ions (1 at%); when the Sr content exceeded 10 at%, the density of grain boundaries increased notably and triple junctions were clearly observed. The dissolution of undoped HA was initiated at crystallite surfaces, whereas the dissolution of Sr-HA started around grain boundaries. Acicular nanocrystal reprecipitation was observed on grain surfaces immersed in simulated body fluid (SBF), while not in dilute hydrochloric acid (HCl). These findings suggest appropriate levels of Sr incorporation can introduce imperfections in the crystal structure of apatite and thus enhance its dissolution rate towards enhanced physicochemical performance in biomedical applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.