Abstract
Nanoindentation provides a convenient and high-throughput means for mapping mechanical properties and for measuring the strain rate sensitivity of a material. Here, nanoindentation was applied to the study of microcrystalline cellulose. Constant strain rate nanoindentation revealed a depth dependence of nanohardness and modulus, mostly attributed to material densification. Nanomechanical maps of storage modulus and hardness resolved the shape and size of voids present in larger particles. In smaller, denser particles, however, where storage modulus varied little spatially, there was still some spatial dependence of hardness, which can be explained by cellulose’s structural anisotropy. Additionally, hardness changed with the indentation strain rate in strain rate jump tests. The resulting strain rate sensitivity values were found to be in agreement with those obtained by other techniques in the literature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.