Abstract

N-doped ordered mesoporous carbon/graphene composites with supercapacitor performance are successful synthesized by evaporation induced self-assembly (EISA). In this procedure, using phenolic resin as carbon source, triblock copolymer (F127) as template, hydrochloric acid as catalyst, tetraethylorthosilicate (TEOS) as structure enhancer agent and urea as additive for improving graphitization and surface wettability, ordered mesoporous carbon is formed by EISA and low temperature carbonization. At the same time, graphene is added into the mixed solution with the carbon source. Transmission electron microscopy (TEM), small-angle X-ray diffraction (XRD) and N2 sorption analysis results illustrate that the samples display two-dimensional ordered mesoporous structure with uniform pore diameter (∼4 nm). The highest surface area could reach to 1801 m2/g and the biggest pore volume can be up to 1.55 cm3/g. The reinforcement of graphitization is implied by the Raman spectroscopy and wide-angle XRD results. The capacitor performance test shows a capacitance of 246 F/g at 1 A/g with excellent stability.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.