Abstract
In order to understand recession behavior and the amount of recession of Lu2Si2O7 in the combustion gas flow, sintered Lu2Si2O7 specimens were manufactured by hot pressing and exposed under various combustion gas flow conditions (T = 1300∼1500°C, P = 0.3 MPa, V = 150 m/s, PH2O = 27∼69 kPa, t = 10 h). After the exposure tests, etch pits, which are assumed to form due to volatilization of SiO2 in the grain boundary phase, were observed at the surface of specimen. The amount of Lu2SiO5 phase at the surface of specimen increased with the increase of gas temperature or water vapor partial pressure. A corresponding decrease in the amount of Lu2Si2O7 phase was observed. Furthermore, by using the average weight loss rate for exposure times of ten hours, the influence of gas temperature and water vapor partial pressure on weight loss rate was examined, and the amount of recession under gas turbine conditions was calculated. Superior environmental resistance was shown relative to Si3N4, SiC and Al2O3.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Society of Materials Science, Japan
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.