Abstract
Porous aluminum was fabricated without the use of a blowing agent by friction stir processing using the gases contained in ADC12 aluminum alloy die-casting plates. The compressive properties of the obtained porous aluminum were investigated. It was shown that a compressive test specimen with a porosity of approximately 70% was obtained that had pores with a relatively small area and high sphericity. Porous aluminum fabricated without the use of a blowing agent exhibited brittle fracture at a relatively high plateau stress and high absorption energy compared with those of ALPORAS.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.