Abstract
Macor® machinable glass-ceramic and commercially pure (cp.) titanium were joined by active metal brazing, using a 64Ag–34.5Cu–1.5Ti (wt.%) filler alloy. The influence of the brazing temperature and holding stage on the microstructure and hardness profile of the interface, as well as on the shear strength of the joint, were assessed. Brazing was performed in a high vacuum furnace at 850, 890 and 930°C for 10 and 30 min. The reaction between the braze alloy and both materials led to the formation of a multilayered interface. The interfacial microstructure was analysed in a scanning electronic microscope (SEM) and the composition of each reaction layer was investigated by energy dispersive X-ray scans (EDS). The interfacial hardness profile was determined by a series of microhardness tests on each reaction layer. The mechanical strength of the joint was assessed from shear tests conducted at room temperature. Brazing at 850°C with a 10 min holding stage produced stronger joints, with an average shear strength of more than 85% of the glass-ceramic bulk strength.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.