Abstract
Sr3Co2Fe24O41 plocrystalline sample was synthesized by using a polymerizable complex method. We investigated the crystallographic and the magnetic properties of sample by using X-ray diffractometer, vibrating sample magnetometer, and Mossbauer spectrometer. Based on the Rietveld refinement, the crystal structure of the sample was found to be single-phased and to be hexagonal with space group of P63/mmc. The hysteresis curves of sample were measured under 15 kOe at various temperatures ranging from 4.2 and 295 K. From the temperature dependence of the magnetization curves under 100 Oe at temperatures between 4.2 and 740 K, three temperature-dependent magnetic transitions were found to have occurred in the Sr3Co2Fe24O41 sample. The Mossbauer spectra of the samples were obtained at various temperatures ranging from 4.2 and 295 K.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.