Abstract
Montmorillonite supported titanium (Ti-MMT) or antimony catalyst (Sb-MMT) has been a hot area of research on preparing polyethylene terephthalate/montmorillonite (PET/MMT) nanocomposites by in situ polymerization. So removal of Ti or Sb from Ti-MMT or Sb-MMT is not expected during in situ polymerization. Studies on immobilization of Ti or Sb on Ti-MMT or Sb-MMT are seldom reported. In this work, a series of montmorillonite supported catalysts of titanium (Ti-MMT) or antimony (Sb-MMT) and cointercalated montmorillonite of titanium and antimony (Ti/Sb-MMT) were prepared by (1) the reaction of sodium bentonite suspension with intercalating solution containing titanium tetrachloride and/or antimony chloride, and (2) drying or calcinating the products at different temperature (100, 150, 240, 350 and 450 °C). The physicochemical properties of these MMT supported catalysts were studied by X-ray diffraction (XRD), fourier transform infrared spectroscopy (FT-IR), inductively coupled plasma optical emission spectrometer (ICPOES), N2 adsorption/desorption isotherms, UV-visible diffuse reflectance spectroscopy(UV-vis) and transmission electron microscopy (TEM). The immobile character of Ti or Sb on MMT supported catalysts was evaluated by a two-step method in deionized water or ethylene glycol. Several results were obtained, i e, (a) during the preparation, with an increase in drying or calcinating temperature, the amount of titanium and/or antimony species remained on these MMT supported catalysts decreased, (b) the experiments about immobile character of Ti or/and Sb showed that with an increase in drying or calcinating temperature, the immobilization of Ti and/or Sb species remained on these MMT supported catalysts increased gradually, (c) Ti-MMT calcinated at 450 °C had the biggest pore volume, which means Ti-MMT had the best adsorption application prospect.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.