Abstract

We found that the adsorption states of Au nanoparticles (NPs) on TiO(2)(110) varied with the ionic liquids (ILs) that encapsulate the NPs during the entire process from synthesis of NPs to immobilization of the NPs on the surface at 323 K. Five kinds of ILs, including three 1-butyl-3-methylimidazolium ([C(4)MIm]) cation-based ILs of tetrafluoroborate ([C(4)MIm][BF(4)]), hexafluorophosphate ([C(4)MIm][PF(6)]) and bis(trifluoromethylsulfonyl)amide ([C(4)MIm][NTf(2)]), and two [BF(4)] anion-based ILs of 1-(methoxymethyl)-1-methylpyrrolidinium ([PY1,1O1][BF(4)]) and N,N-diethyl-N-methyl-N-(2-methoxyethyl) ammonium ([N122,1O2][BF(4)]), were used. They provided different adsorption states of the Au NPs on the surface. We considered the determinant factor for the adsorption states of NPs on the surface from the viewpoint of electrostatic interactions between IL and IL and between IL and the surface. We deduced the influence of these interactions from the increments of NP's diameter and the amount of NPs after the immobilization, and obtained the order of anions as [BF(4)] ≈ [NTf(2)] > [PF(6)] for the three [C(4)MIm] based ILs and the order of cations as [PY1,1O1] > [C(4)MIm] > [N122,1O2] for the three [BF(4)] based ILs. Interestingly, the above orders were no match with the conventional physicochemical and chemical parameters but β of Kamlet-Taft solvent descriptors and Lewis basicity of anions in the case of anions of ILs. The results of anions indicate that the chemical natures of ILs might affect the immobilization of NPs through hydrogen bonding or coordination bonding with the surface. We suggested that such a trend in anions was 'local viscosity' of ILs in the vicinity of surface. Besides, layer formation of IL on the surface might be also an influential factor to control the size of NPs and the surface density of NPs. Our results show that the combination of a charged surface and charged molecules has the potential for controlling locations of the NPs on the surface preferentially with tuning the electrostatic interaction.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.