Abstract
AbstractUHMWPE samples were implanted with metal and metal-gas hybrid ions (Ag, Ag+N, C+H, C+H+Ar, Ti+O ) by using improved MEVVA Ion implantation technique [1,2]. with an extraction voltage of 30 kV and fluence of 1017 ions/cm2 in an attempt to change their surface morphologies in order to understand the effect of ion implantation on the surface properties of UHMWPEs. Characterizations of the implanted samples with RBS , ATR - FTIR, spectra were compared with the un-implanted ones. Implanted and unimplanted samples were also thermally characterized by TGA and DSC. It was generally observed that C-H bond concentration seemed to be decreasing with ion implantation and the results indicated that the chain structure of UHMWPE were changed and crosslink density and polymer crystallinity were increased compared to unimplanted ones resulting in increased hardness. It was also observed that nano size cracks (approx.10nm) were significantly disappeared after Ag implantation, which also has an improved antibacterial effect. Contact angle measurements showed that wettability of samples increased with ion implantation. Results showed that metal and metal+gas hybrid ion implantation could be an effective way to improve the surface properties of UHMWPE to be used in hip and knee prosthesis.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.