Abstract
Three-dimensional (3D) needled carbon/carbon (C/C) composites with a lowest porosity of 15.6% were achieved after 1 cycle of impregnation by phenolic resin slurry containing graphite filler, hot-pressing curing and pyrolysis. Carbon/silicon carbide (C/SiC) composites were obtained by liquid silicon infiltrating C/C composites. The aim was to incorporate cost effectiveness and excellent performance of C/SiC braking material. Using filler content not exceeding 30 wt% in the slurry promised undamaged C/C segments in C/SiC composites. The linear wear rate of C/SiC using 30 wt% filler was 0.33 μm side −1 cycle −1 and displayed a fourfold decrease; its weight wear rate was 2.46 mg side −1 cycle −1 and minus 171%, compared with the previously reported values of C/SiC without filler, at a braking velocity of 28 m/s. Its friction coefficients and friction stability coefficients appeared relative insensitive to changes in braking velocities and displayed higher values at high braking velocities compared with the previous values.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.