Abstract
Microstructure evolution during the supersolvus heat treatment of a powder-metallurgy, low-solvus, high-refractory (LSHR) superalloy was established. For this purpose, three lots of LSHR with varying initial carbon/boron composition and thermomechanical history were subjected to a series of short-time (induction) and long-time (furnace) heat treatments followed by scanning electron microscopy/electron backscatter diffraction and quantitative metallography. The size of the (pinned) gamma grains exhibited a limited dependence on heating rate and soak time at peak temperature, and it was generally smaller than the predictions based on the classic Smith-Zener model. The differences were rationalized in terms of stereological and pinning-particle location effects. Observations of limited coarsening of the carbide/boride pinning particles were interpreted in the context of prior experimental observations and a modified Lifshitz-Slyosov-Wagner model applied previously for the coarsening of compound phases in steels.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.