Abstract
Abstract The biomedical co-continuous (β-TCP+MgO)/Zn-Mg composite was fabricated by infiltrating Zn-Mg alloy into porous β-TCP+MgO using suction exsorption technique. The microstructure, mechanical properties and corrosion behaviors of the composite were evaluated by means of scanning electron microscopy (SEM), X-ray diffraction (XRD), mechanical testing, electrochemical and immersion test. It was found that the molten Zn-Mg alloy had infiltrated not only into the pores but also into the struts of the porous β-TCP+MgO scaffold to form a compact composite. The Zn-Mg alloy contacted to the β-TCP+MgO scaffold closely, and no reaction layer can be found between the alloy and the scaffold. The compressive strength of the composite was as high as 244 MPa, which was about 1000 times higher than that of the original porous β-TCP+MgO scaffold and 2/3 of the strength of the Zn-Mg bulk alloy. The electrochemical and immersion tests in simulated body fluid (SBF) solution indicated that the corrosion resistance of the composite was better than that of the Zn-Mg bulk alloy. The corrosion products on the composite surface were mainly Zn(OH) 2 . Appropriate mechanical and corrosion properties indicated that the (β-TCP+MgO)/Zn-Mg composite fabricated by suction exsorption would be a very promising candidate for bone substitute.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.