Abstract
Abstract To get a full understanding of hot extrusion, solid solution treatment and aging process on the Al−0.56Mg− 0.63Si alloy, the microstructure and mechanical properties of a U-shaped profile were studied through optical microscopy, scanning electrical microscopy, transmission electrical microscopy, hardness, and tensile tests. The coarse equiaxed grains existed near the profile edge as a result of the dynamic recrystallization nucleation and exceeding growth during hot extrusion. The fibrous deformed and sub-structured grains located between the two coarse grain layers, due to the occurrence of work-hardening and dynamic recovery. Perpendicular needle β′′ precipitates were distributed inside the grain, and obvious precipitates-free zone appeared after aging treatment. The tensile strength, yield strength and elongation of the aged Al−Mg−Si alloy U-shaped profile were no less than 279.4 MPa, 258.6 MPa, and 21.6%, respectively. The fracture morphology showed dimple rupture characteristics. The precipitates and grain boundaries played key role in the strengthening contribution.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.