Abstract
The tube of titanium and the bar of NiCr alloy were bonded through explosive cladding technique; a good quality bonding was obtained. Melting zones are encountered in sections of the explosive cladding interface, and they serious affect the properties of the explosive cladding composite. Microstructure of melting zone in the interface of Ti/NiCr explosive cladding bar were investigated by means of optical microscope (OM), scanning electron microscope (SEM) and microhardness as well as using micro-focus X-ray diffraction and electron probe analyses. The results show that the melting zone is composed of intermetallics of brittle and stiff, and there is no element diffusion during explosive cladding process. The tendency of composition segregation of melting zone is decreased. The solidification rate and the actual distribution coefficient of solute in the melting zone of Ti/NiCr explosive cladding interface are not less than 0.1×108k/s and 1 respectively. The formation of microstructure in the melting zone is result from the high solidification rate in the explosive cladding interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.