Abstract
This paper describes the stability of microstructure in normalized and tempered modified 9Cr–1Mo steel exposed to service temperatures in the range of 773–873 K for different time durations. A detailed microstructural and microchemical analysis of the secondary phases was carried out using optical and electron microscopy techniques. The microstructural observations, supported by hardness measurements showed that the lath morphology of the tempered martensite was retained even after 10 000 h of aging. The coarsening of M 23C 6 carbide was observed until 5000 h, when the Laves phase started appearing. The microstructural features observed are discussed in conjunction with the embrittlement observed in this steel on high temperature aging exceeding 5000 h.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.