Abstract
The present paper describes processing, microstructures and phase relationships in directionally solidified Cr 2NbNb and Cr 2NbCr eutectics. Both of these eutectics, and the stoichiometric Laves phase Cr 2Nb, were directionally solidified using cold crucible Czochralski crystal growth with growth rates from 1 to 15 mm/min. Cr 2NbNb had a rod/ribbon-type structure and Cr 2NbCr had a lamellar structure. The crystallographic oreintation relationships between both Cr and Nb and the Cr 2Nb Laves phase in the individual eutectics were characterized using transmission electron microscopy. Inter-phase orientation relationships in these eutectics were complicated by the transformation of Cr 2Nb from the C14 to the C15 crystal structure on post-solidification cooling. Twins were observed in the C15 Cr 2Nb phase in both the single phase and eutectic samples. The relationship between the twins, the C14–C15 transformation, and the eutectic morphology is also discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.