Abstract
Processes for potential-induced degradation (PID) and recovery phenomena were characterized using p-type multicrystalline Si photovoltaic modules and by PID test method using Al plate. Very severe PID phenomena accompanied with a drastic reduction in both open-circuit voltage and shunt resistance were observed within only several hours. It was found that PID phenomena are strongly accelerated at higher temperature and under higher negative-voltage application, on the other hand, PID phenomena do not necessarily require high humidity in this test method using Al plate. Na diffusion from the cover glass to the Si cell was observed after PID test. Recovery process from PID was also observed by applying positive voltage. However, complete recovery of photovoltaic performances was observed at room temperature in the dark without positive-voltage application for test modules with PID although recovery process requires a few hundred days.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.