The aim of this work was a scanning electron microscopy (SEM) evaluation of the hardness and morphological changes of enamel irradiated by neodymium: yttrium aluminium garnet (Nd:YAG) laser with different energy levels. Twenty-eight human teeth samples were divided into 4 groups: control, where enamel surface was not lased, and 3 test treated with 3 different levels of energy power 0.6, 1.2 and 2.4 Watt, respectively. In each group, 5 samples underwent Vickers micro-hardness test and 2 samples were processed for SEM. No significant differences between treated and non treated samples were found by micro-hardness test. However, by SEM, test samples showed a rougher enamel surface than control. Specifically, the 0.6 Watt treated samples showed vertical scratches and glass-like areas, while in the other 2 groups enamel surface was covered by craters and cracks. These findings suggest that enamel should be lased at a low energy level to preserve its integrity and reduce demineralization, and thus for dental caries prevention purposes; while high energy level creates a retentive surface suitable for sealant or composite anchorage.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.