Abstract
A series of mesoporous alumina was prepared using a selected group of anionic, non-ionic, and cationic surfactants with Al-tri- sec-butoxide or Al 3+ in organic solvent with stoichiometric amount of water, and in aqueous solution with different hydrolyzing agents, or with complexing agent at room temperature to 100 °C. A comparison of the physicochemical properties of the materials prepared was made with respect to surface area, thermal stability, and porosity. Anionic surfactants in aqueous solution produced thermally unstable materials but in organic solvent resulted in a moderately stable alumina phase. Both cationic and non-ionic surfactants produced thermally stable mesoporous alumina after removal of the surfactant upon calcination at 500 °C when the materials were synthesized in organic solvents. Overall, mesoporous alumina prepared with cationic cetyltrimethylammonium bromide in sec-butanol in the optimized substrate composition of Al:surfactant:H 2O:solvent = 1.0:0.3:2.0:15 exhibited the best textural property among the various synthesis systems investigated.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.