Abstract
In this work the effects of stirring/vigorous shearing on matrix and graphite phase in nodular cast iron melt during solidification were studied. Several experiments were conducted for different cooling and stirring times. Samples were prepared and examinations of the microstructure were conducted and compared using Leica Optical Microscope and Scanning Electron Microscope (SEM). In addition, a chemical analysis of the graphite precipitate was performed using EDX equipment mounted on SEM. Oxidation of the melt and formation of oxide nuclei during stirring were observed and analysed. The influence of melt shearing on the structure, nodule count, distribution, area fraction and on overall graphite precipitation was observed and examined with the help of respective computer programs and soft wares. Stirring resulted in increasing the nucleation sites for graphite precipitation thereby increasing the nodule count and area fraction of carbide and transforming the structure from pearlitic matrix to ferritic matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.