Abstract
This study evaluated the reliability and failure modes of anterior implants with internal-hexagon (IH), external-hexagon (EH), or Morse taper (MT) implant-abutment interface designs. The postulated hypothesis was that the different implant-abutment connections would result in different reliability and failure modes when subjected to step-stress accelerated life testing (SSALT) in water. Sixty-three dental implants (4 × 10 mm) were divided into three groups (n = 21 each) according to connection type: EH, IH, or MT. Commercially pure titanium abutments were screwed to the implants, and standardized maxillary central incisor metallic crowns were cemented and subjected to SSALT in water. The probability of failure versus number of cycles (95% two-sided confidence intervals) was calculated and plotted using a power-law relationship for damage accumulation. Reliability for a mission of 50,000 cycles at 150 N (90% two-sided confidence intervals) was calculated. Polarized-light and scanning electron microscopes were used for failure analyses. The beta values (confidence intervals) derived from use-level probability Weibull calculation were 3.34 (2.22 to 5.00), 1.72 (1.14 to 2.58), and 1.05 (0.60 to 1.83) for groups EH, IH, and MT, respectively, indicating that fatigue was an accelerating factor for all groups. Reliability was significantly different between groups: 99% for MT, 96% for IH, and 31% for EH. Failure modes differed; EH presented abutment screw fracture, IH showed abutment screw and implant fractures, and MT displayed abutment and abutment screw bending or fracture. The postulated hypothesis that different implant-abutment connections to support anterior single-unit replacements would result in different reliability and failure modes when subjected to SSALT was accepted.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: The International Journal of Oral & Maxillofacial Implants
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.