Abstract
The mechanical properties and deformation mechanisms of nano-porous ZnO thin films electrodeposited on glass substrates were determined by nanoindentation and in situ scanning electron microscope (SEM) micropillar compression. The intragranular nature of the nanoscale porosity within the individual mono-crystals of the films was probed at nano- and micro-scales for determining their mechanical response. The hardness (3.5GPa) and reduced elastic modulus (65GPa) of the compact thin film were found to decrease by increasing the intragranular porosity controlled by the electrochemical deposition potential of ZnO. Focused ion beam (FIB) cross-sections of residual imprints reveal that the decrease in hardness and elastic modulus observed is primarily due to compaction of the nano-porous structure. In situ SEM compression of FIB machined micropillars reveals brittle fracture and near theoretical strengths in the compact film (~2GPa), and a higher flaw tolerant response despite lower failure stress in the most porous film.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.