Abstract

The mechanical behavior of Zr-based bulk amorphous alloy composites (BAACs) was investigated at 77 K. The 5 vol. % Ta-BAAC maintained large plastic strains of approximately 13% with a 16% strength increase, when compared with that at 298 K. The interaction between shear bands and particles shows that shear extension in particles has limited penetration, and shear bands build up around particles. In addition to on the failure surface of the amorphous matrix, molten characteristics were also found on the surface of sheared particles. Pair distribution function studies were performed to understand the mechanical behavior.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.