Abstract
The tribological behavior of AlCr0.5NbTaxTi4–x (x = 0, 0.5, and 1) refractory high-entropy alloys was systematically investigated from room temperature to 800 °C. The relationship between the alloy composition, microstructure, mechanical properties, and tribological performance was analyzed. The results show that all three alloys have a body-centered cubic (bcc) single-phase structure. The Ta addition enhances solid solution strengthening and increases the melting point that would resist high-temperature thermal softening. As a result, high-temperature strength is enhanced considerably, the coefficients of friction (COF) and wear rates of the alloys are reduced considerably at elevated temperatures, demonstrating excellent friction-reducing and anti-wear properties, e.g., the COF and wear rate of AlCr0.5NbTaTi3 alloy at 800 °C are 0.34 and 4.40 × 10–7 mm3 N–1 m–1, respectively. The excellent wear resistance at high temperatures can be attributed to the formation of an oxide-tribo layer (Ta2O5 and TiO2) with ultrafine-grained layers and good high-temperature mechanical properties.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.