Magnetocaloric effect and magnetic properties of Tb0.9Sn0.1MnO3

Abstract

The magnetocaloric effect in magnetic materials is of great interest nowadays. In this article we present an investigation about the magnetic properties near the magnetic transition in a polycrystalline sample of a manganite Tb0.9Sn0.1MnO3. Particularly, we are interested in describing the nature of the magnetic interactions and the magnetocaloric effect in this compound. The temperature dependence of the magnetization was measured to determine the characteristics of the magnetic transition and the magnetic entropy change was calculated from magnetization curves at different temperatures. The magnetic solid is paramagnetic at high temperatures. We observe a dominant antiferromagnetic interaction below Tn=38 K for low applied magnetic fields; the presence of Sn doping in this compound decreases the Néel temperature of the pure TbMnO3 system. A drastic increase in the magnetization as a function of temperature near the magnetic transition suggests a strong magnetocaloric effect. We found a large magnetic entropy change ΔSM(T) of about −4 J/kg K at H=3 T. We believe that the magnetic entropy change is associated with the magnetic transition and we interpret it as due to the coupling between the magnetic field and the spin ordering. This relatively large value and broad temperature interval (about 35 K) of the magnetocaloric effect make the present compound a promising candidate for magnetic refrigerators at low temperatures.