Abstract
The magnetic domain structure is studied in epitaxial Fe100-xGax/MgO(001) films with 0 < x < 30 and thicknesses below 60 nm by magnetic force microscopy. For low gallium content, domains with the magnetization lying in the film plane and domain walls separating micrometric areas are observed. Above x ≈ 20, the magnetic contrast shows a fine corrugation, ranging from 300 to 900 nm, suggesting a ripple substructure with a periodic oscillation of the magnetization. We discuss the presence of a random magnetic anisotropy contribution, that superimposed to the cubic coherent anisotropy, is able to break the uniform orientation of the magnetization. The origin of that random anisotropy is attributed to several factors: coexistence of crystal phases in the films, inhomogeneous distribution of both internal strain and Ga–Ga next nearest neighbor pairs and interface magnetic anisotropy due to the Fe–O bond.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.