Abstract
AbstractFlat and wrinkled La0.7Sr0.3MnO3 (LSMO) thin films were prepared by sol‐gel method, respectively, on Si (001) substrates by adjusting heating rate at drying stage. Wrinkled film has larger grains than flat film. Coercive field (about 27 Oe) of wrinkled film is higher than that of flat film, which is much low as around 5 Oe. Compared with flat films, wrinkled films have larger magnetization, higher Curie temperature (334 K) and peak resistivity temperature (243 K), and lower resistivity (0.18 Ohm·cm at 300 K). The introducing of wrinkles is an efficient way to induce compressive stress in sol‐gel derived polycrystalline LSMO films and enhance the magnetic and electric properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.