Abstract
The reverse transformation of austenite from pearlite was observed in-situ by using a sophisticated EBSD system. Quantitative information on the nucleation sites and orientation selection of the austenite was obtained. Initially, the nucleation sites were restricted to high-angle grain boundary (HAB) and all the austenite orientations were selected by Kurdjumov-Sachs (K-S) orientation relationship. Latterly, the constraints were relaxed as new nucleation sites were involved. The γ growth was preferentially into the pearlite grains without K-S relation. Nucleation and growth at HAB edge may contribute to γ coarse grains, whereas nucleation at pre-existing γ boundary is important to grain refinement of γ structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.