Abstract
High-performance YBCO 123 (YBa2Cu3O7-x) bulk superconductor samples were produced using the 3D printing paste-extrusion technique. The YBCO powder obtained after sintering a pre-mixture of Y2O3, BaCO3 and CuO powders at 950 °C was used in the formulation of pastes for extrusion in a 3D freeform printer. The 3D samples printed from pastes containing the pre-mixture powders were sintered, while those produced using the YBCO powder were not. X-ray diffraction (XRD), energy dispersive spectroscopy (EDS) and Raman analysis all confirmed the YBCO phase after sintering, both in the powder and in the samples made with the pre-mixture. Scanning electron microscopy (SEM) images revealed powder grains of heterogeneous size and geometry, as well as grain aggregation, in the sintered samples. Superconducting quantum interference device (SQUID) measurements taken within a fixed magnetic range revealed that the printed pieces have a typical magnetization temperature of 92 K, reaching −1.43 emu/g and −1.59 emu/g respectively a zero-field-cooled magnetization (ZFC) for sintered and non-sintered printed samples.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.