Abstract
Abstract The high cycle fatigue (HCF) behaviour and load sequence effects in HCF of two microalloyed steels are presented. Dislocation structures that resulted from HCF loading were examined. The fatigue limits of the two microalloyed (MA) steels (non-failure after 2 × 106 cycles) correlated well with the cyclic yield strength. The results of two-step loading showed that in both the steels after an initial life fraction of approximately 0.4, the residual life deviated significantly from that predicted by the Palmgren-Miner rule. Crack initiation lives of the MA steels had been determined from the two-step loading experiments. Fatigue functions, which can be used for life prediction under complex loading conditions using the consecutive Wohler curve approach, were determined from the two-step loading tests. Dislocation cell structures were observed near the fracture surface in the HCF regime. At the fatigue limit, dislocation dipoles and loops were seen.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.