Abstract
LiNO3 addition to the cement solidified miscellaneous wastes has been proposed for preventing hydrogen ges generation caused by the corrosion of aluminum materials contained in the wastes. To determine an additive among alkaline metal ions, galvanic current was measured in 0.1 M alkaline metal hydroxide solution between aluminum and platinum electrodes. The volume of hydrogen gas generated from an aluminum specimen was measured in a KOH solution with LiNO3, LiCl, LiBr, Li2CO3 or Li2SO4 to decide the best additive. Applicability of the chosen additive to cement was confirmed by hydrogen gas generation measurement from an aluminum specimen in cement paste. The prevention mechanism was analyzed by X-ray diffraction, SEM and SIMS. The current measured in LiOH solution decreased with time, then reached 0 μA/mm2, while the current was detected in other alkaline metal hydroxide solutions. The least volume of hydrogen gas generation was measured in a KOH solution with LiNO3. The volume of generated hydrogen gas i...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.