AbstractAl-Li alloy 2198 exhibits good combination of toughness and strength but its application is strongly limited by the poor weldability due to the formation of porosities during fusion-welding. This is the first study proposing and verifying a new approach to produce defect-free laser welds of poorly fusion-weldable Al-Li alloy 2198 with applied external pressure, i.e., feasibility of laser pressure welding to Al-Li alloy 2198 was examined. The microstructures associated with tensile shear behavior of laser pressure welded Al-Li alloy 2198 obtained at various welding parameters were analyzed. The results showed that formation of the welding defect in the weld could be successfully suppressed by applying laser pressure welding, even without shielding gas. Three microstructural zones, including the chill zone, the columnar zone and the equiaxed zone were observed in the fusion zone. Size of fusion zone and area fraction of porosities generally increased with increasing roller pressure and welding heat-input, and they dominantly affected the tensile shear behavior, including the peak load and the failure mode, of the weld.
Highlights
Al-Li alloy 2198 exhibits good combination of toughness and strength but its application is strongly limited by the poor weldability due to the formation of porosities during fusion-welding
The peak load increased with increasing roller pressure at high welding heat-input, but this effect is not significant at low welding heat-input. 2 different failure modes were detected in the specimens: the pull-out failure mode with fracture along the fusion boundary (Figure 8a), and the interface failure mode with fracture along the interface (Figure 8b)
The fusion zone consisted of three microstructural zones, i.e., the chill zone, the columnar zone, and the equiaxed zone
Summary
Abstract: Al-Li alloy 2198 exhibits good combination of toughness and strength but its application is strongly limited by the poor weldability due to the formation of porosities during fusion-welding. This is the first study proposing and verifying a new approach to produce defect-free laser welds of poorly fusion-weldable Al-Li alloy 2198 with applied external pressure, i.e., feasibility of laser pressure welding to Al-Li alloy 2198 was examined. The microstructures associated with tensile shear behavior of laser pressure welded Al-Li alloy 2198 obtained at various welding parameters were analyzed. Size of fusion zone and area fraction of porosities generally increased with increasing roller pressure and welding heat-input, and they dominantly affected the tensile shear behavior, including the peak load and the failure mode, of the weld
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.