Abstract

Very long wavelength infrared (VLWIR; 15 to 17 µm) detectors are required for remote sensing sounding applications. Infrared sounders provide temperature, pressure and moisture profiles of the atmosphere used in weather prediction models that track storms, predict levels of precipitation etc. Traditionally, photoconductive VLWIR (λc >15 µm) detectors have been used for sounding applications. However, photoconductive detectors suffer from performance issues, such as non-linearity that is 10X – 100X that of photovoltaic detectors. Radiometric calibration for remote sensing interferometry requires detectors with low non-linearity. Photoconductive detectors also suffer from non-uniform spatial optical response. Advances in molecular beam epitaxy (MBE) growth of mercury cadmium telluride (HgCdTe) and detector architectures have resulted in high performance detectors fabricated in the 15 µm to 17 µmm spectral range. Recently, VLWIR (λc ∼ 17 µm at 78 K) photovoltaic large (1000 µm diameter) detectors have been fabricated and measured at flux values targeting remote sensing interferometry applications. The operating temperature is near 78 K, permitting the use of passive radiators in spacecraft to cool the detectors. Detector non-AR coated quantum efficiency >60% was measured in these large detectors. A linear response was measured, while varying the spot size incident on the 1000 µm detectors. This excellent response uniformity, measured as a function of spot size, implies that low frequency spatial response variations are absent. The 1000 µm diameter, λc ∼ 17 µm at 78 K detectors have dark currents ∼160 µA at a −100 mV bias and at 78 K. Interfacing with the low (comparable to the contact and series resistance) junction impedance detectors is not feasible. Therefore a custom pre-amplifier was designed to interface with the large VLWIR detectors operating in reverse bias. A breadboard was fabricated incorporating the custom designed preamplifier interfacing with the 1000 µm diameter VLWIR detectors. Response versus flux measurements were made on the large VLWIR detectors and non-linearity <0.15% was measured at high flux values in the 2.5×1017 to 3.5×1017 ph-cm−2sec−1 range. This non-linearity is an order of magnitude better than for photoconductive detectors.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.