Abstract

Extensive morphological studies on a syndiotactic polystyrene (sPS) sample prepared from compression molding were carried out using small-angle X-ray scattering (SAXS) and transmission electron microscopy (TEM). SAXS was conducted at 25 ○C as well as at 150 ○C to enhance the scattering contrast in order to obtain more reliable morphological parameters. The compression-molded sample was crystallized into a β′ orthorhombic crystal lattice characterized by wide-angle X-ray diffraction (WAXD). A similar weight fraction of crystallinity, ca. 0.37, was obtained from both WAXD and differential scanning calorimetry measurements.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.