Abstract
Abstract Graphene oxide (GO) sheets were obtained via an improved Hummer's method, and the Poly(vinylidene fluoride) (PVDF)/GO membranes employing GO as nucleating agent were prepared by solution casting. The crystalline behaviors and the crystallization kinetics of PVDF/GO membranes with varying GO concentration were investigated after isothermal crystallization at different temperatures. The results showed that the addition of GO induced the β-phase formation of PVDF. The spherulite diameter reached the peak value when the content of GO was 0.1 wt%, then reduced to the minimum value at 1 wt% GO within the tested temperature range of isothermal crystallization. It is worth mentioning that the relative fraction of β phase F(β) was dramatically improved to 0.85 for the PVDF/GO membrane with 0.5 wt% GO at 155°C. Furthermore, an enhancement of the crystallization rate was observed as the contents of GO increased in the system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.