Abstract
Temperature dependent threshold voltage (Vth) variation of GaN/AlGaN/Gd2O3/Ni-Au structure is investigated by capacitance-voltage measurement with temperature varying from 25°C to 150°C. The Vth of the Schottky device without oxide layer is slightly changed with respect to temperature. However, variation of Vth is observed for both as-deposited and annealed device owing to electron capture by the interface traps or bulk traps. The Vth shifts of 0.4V and 3.2V are obtained for as-deposited and annealed device respectively. For annealed device, electron capture process is not only restricted in the interface region but also extended into the crystalline Gd2O3 layer through Frenkel-Poole emission and hooping conduction, resulting in a larger Vth shift. The calculated trap density for as-deposited and annealed device is 3.28×1011∼1.12×1011 eV−1cm−2 and 1.74×1012∼7.33×1011 eV−1cm−2 respectively in measured temperature range. These results indicate that elevated temperature measurement is necessary to characterize GaN/AlGaN heterostructure based devices with oxide as gate dielectric.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.